|Título:||Ion-exchange voltammetry with nafion/poly(sodium 4-styrenesulfonate) mixed coatings on mercury film electrodes: Characterization studies and application to the determination of trace metals|
|Autor:||Rocha, L. S.|
Pinheiro, J. P.
Carapuça, H. M.
|Editora:||American Chemical Society|
|Citação:||Rocha, L. S.; Pinheiro, J. P.; Carapuça, H. M. Ion-exchange voltammetry with nafion/poly(sodium 4-styrenesulfonate) mixed coatings on mercury film electrodes: Characterization studies and application to the determination of trace metals, Langmuir, 22, 19, 8241-82, 2006.|
|Resumo:||This work aimed to produce improved polymer coatings for the modification of thin mercury film electrodes (TMFEs). The goal is to obtain sensitive, reproducible, mechanically stable and antifouling devices suitable for the determination of trace metal cations in complex media. Therefore, novel mixed coatings of two sulfonated cationexchange polymers of dissimilar characteristicssNafion (NA) and poly(sodium 4-styrenesulfonate) (PSS)swere produced by solvent evaporation onto glassy carbon electrodes. The effect of the mass ratio (NA:PSS) on the film morphology was studied by scanning electron microscopy, revealing the formation of biphasic polymer systems, where PSS bead-shaped clusters appeared randomly dispersed into a uniform and compactNAenvironment. The permselectivity/ ion-exchange features of the mixed films onto glassy carbon were evaluated using cathecol, urate, and dopamine. To allow trace metal analysis, thin mercury films were plated through the NA/PSS coatings, being the reproducibility and ion-exchange features of the mixed coatings-TMFE evaluated using lead ions. The best NA/PSS coating was found for the mass ratio of 5.3. Analytical performance of the NA/PSS-TMFE yielded a detection limit of 5.5 nM (3ó), and the application of this modified electrode to an untreated polluted estuarine water sample produced significant improvements in the quality of the signal compared with that for a bare TMFE.|
|Aparece nas colecções:||FCT2-Artigos (em revistas ou actas indexadas)|
Ficheiros deste registo:
|n32_Langmuir 22 (2006) 8241.pdf||380,89 kB||Adobe PDF||Ver/Abrir Acesso Restrito. Solicitar cópia ao autor!|
Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.